Hostacom TYC727N PARCHMENT high melt flow, 2,000 MPa flexural modulus, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of processability, rigidity, impact, and scratch and mar resistance. It is typically used for molded-in color automotive instrument panels that require high durability.
Hostacom TYC727N PARCHMENT
Description
Availability
North America
Legend
SDS - Safety Data Sheet
PSB - Product Stewardship Bulletin
Product Data and Technical Information
| Melt Flow Rate (230 °C/2.16 kg) | 28 g/10 min |
| Density (23 °C) | 1.02 g/cm³ |
| Flexural Modulus | 2000 MPa |
| Tensile Stress at Yield | 23 MPa |
| Tensile Strain at Yield | 8 % |
| Notched Izod Impact Strength (23 °C) | 30 kJ/m² |
| Notched Izod Impact Strength (-40 °C) | 3.5 kJ/m² |
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 110 °C |
| Deflection Temperature Under Load (1.80 MPa, Unannealed) | 57 °C |
| Coefficent of Linear Thermal Expansion (CLTE), Flow (-22 to 212 °F, -30 to 100 °C) | 4.8 x 10-5 cm/cm/°C |
| Mold Shrinkage |
Technical Data Sheet
Technical Data SheetProcess
Injection Molding
Resin
Polypropylene Compounds
Applications
Instrument Panels, Interior Automotive Applications
Prohibited Applications of Compounded Polyolefins:
The following applications and/or end uses are prohibited by LyondellBasell. LyondellBasell will not solicit the sale of, or knowingly supply, product for use in the following applications:
FDA Class III medical devices, European Class III medical devices, Health Canada Class IV Medical Devices, applications involving permanent implantation into the body & life-sustaining medical applications